火电厂锅炉管内壁氧化皮脱落模型研究及应用

yanxying · 发表于 2013-2-19 09:07:06

火电厂锅炉管内壁氧化皮脱落模型研究及应用
孙玺刘晓丹杜保华王大鹏赵晋松李耀君刘振宇
西安热工研究院有限公司，陕西西安710032
摘要：
通过分析影响火电厂锅炉管内壁氧化皮脱落的关键因素，设计了一种可应用于工程实
际的氧化皮脱落模型，开发了基于B/S 结构的火电厂高温受热面氧化皮脱落风险预警系统，
将其应用于多家电厂，实践证明系统提示的氧化皮脱落高风险区和现场割管检测的结果基
本吻合。
关键词：锅炉管氧化皮应变脱落风险预警系统
Study and Application of Boiler Tube Inner Oxide Scale Spalling Modle in Power
Plant
Sun Xi,Liu Xiaodan,Du Baohua,Wang Dapeng, Zhao Jinsong,Li Yaojun，Liu Zhenyu
Xi’an Thermal Power Research Institute Co Ltd, Xi’ an 710032, Shaan xi
Province, PRC
Abstract:
By analyzing the key factors of the boiler tube inner oxide spalling in power
plant，an oxide spalling model has been designed and applied to actual projects.
B / S structure-based boiler tube inner oxide scale spalling risk warning system
has been developed and applied in several power plants, practice has proven that
the warning results produced by the system and the inspect result on site are almost
constant.
Key words: boiler tube, oxide, strain, spalling risk, warning system
前言
近年来，大批高参数超临界、超超临界机组相继投产，1Cr18Ni9Ti、12X18H12T、TP304H、
TP347H、TP316H 等18-8 系列粗晶奥氏体不锈钢在超临界和超超临界机组上广泛应用，然而
这些机组的过热器、再热器其蒸汽侧氧化皮在停炉时容易发生大面积脱落，脱落的氧化皮
一方面可能堵塞在管子的“U”型弯头位置，使通流面积减小，致使管子壁温上升出现爆管；
另一方面氧化皮随同蒸汽流进入汽缸内部还会造成汽轮机喷嘴、叶片、叶轮、隔板等部件
的异常冲蚀和磨损。这些问题已经成为大型火电机组安全经济运行的重大威胁。
在预防控制氧化皮脱落和堵塞的方面，国内外科研机构做了很多研究。1978 年ARMITT